PO-56120 MMA Structural adhesive

third generation, advanced, slow cure, two-part 10:1 Methacrylate metal-bonding adhesive, meeting all three highest metal bonding standards for automotive industry.
Request a Quote

Products Details

PO series MMA structural adhesive

Glue

Description 

Color

Ratio

Viscosity (cps)

Working time (minutes)

Fixture time (minutes)

PO-0419

For bonding metal

Grey

10:1

A: 100,000 - 130,000
B: 20,000 - 50,000

4-6

17-19

PO-1132

For bonding metal, medium cure

Grey

10:1

A: 100,000 - 130,000
B: 20,000 - 50,000

11-13

28-32

PO-1852

For bonding metal, medium cure

Grey

10:1

A: 120,000 - 150,000
B: 20,000 - 50,000

18-22 

48-52

PO-2775

For bonding metal, Long cure

Grey

10:1

A: 130,000 - 170,000
B: 20,000 - 50,000

27-33 

65-75

PO-56120

For bonding metal, long cure

Grey

10:1

A: 170,000 - 210,000
B: 20,000 - 50,000

56-64 

100-120

General Description

UVALAM PO-56120 is a third generation, advanced, slow cure, two-part 10:1 Methacrylate metal-bonding adhesive.

UVALAM PO-56120 can be used for structurally bonding metals without a primer and engineering plastics and composite assemblies with little to no surface preparation.

UVALAM PO-56120 provides a well balanced performance in a broad temperature range and is one of very a few products in the world that can meet all three highest metal bonding standards for automotive industry.

UVALAM PO-56120 is designed with the advanced technology in the world and manufactured in China with the most advanced process and with imported raw materials.

Typical Characters 

Working Time at 24:       56-64 minute

Fixture Time at 24:          100-120 minute

Operating Temperature:   -5° C – 12

Gap Filling Capacity:         up to 9 mm

Mixed Density:                   0.98 g/cm3 

Physical Properties

 

             Part-A

            Part-B

Viscosity at 24℃

100,000 – 130,000

20,000 – 50,000

Color

Off-White    

Grey

Density at 24℃ 

0.96 g/cm3 

1.08 g/cm3 

Mix Ratio by Volume

10

1.0

Mix Ratio by Weight

8.9

1.0

Chemical Resistance

1/ Excellent resistance to:            2/ Susceptible to:

Acids and Bases (3-10pH)              Polar Solvents

Hydrocarbons                                  Strong Acids and Bases

Salt Solutions

Recommended for

Metals: Aluminum, CRS, Stainless Steel

Engineering Plastic: ABS, Acrylics, Polycarbonate, PVC

FRP: Epoxy-based, Polyester-based, Vinyl Ester-based, PU-based

Cartridge packing size: 

Dual 10:1 PBT cartridge 50ml;

Dual 10:1 PBT cartridge 490ml.  

Storage & Shelf life:

The shelf life of PPO-56120 stored at 20 ± 4is 12 months from the date of manufacture. Cool storage at around 12 can extend the shelf life. Long-term exposure above 25 will reduce the shelf life. Prolonged exposure of activators, including cartridges that contain activators, above 35 quickly diminishes the reactivity of the product, and should be avoided. This product should never be frozen.   

 

📞📞📞